Crystallization and Melting of Nylon 610

Differential scanning calorimetry was used to study the crystallization andmelting of nylon 610.

For nylon 610 crystallized from the melt state (260℃), the overall rateof bulk crystallization can be described by a simple Avrami equation with Avrami exponentn ≈ 2, independent of crystallization temperature.

With the experimentally obtainedTm0 (235℃ ~ 255℃) of nylon 610, the fold surface free energy σe was determined to be35 ~38 erg/cm2.The effects of annealing temperature and time on the melting of quenched nylon 610 were also investigated.

For nylon 610 quenched at room temperature there is only one DSC endotherm peak DSC scans on annealed samples exhibited an endotherm peak at approximately 10℃ above the annealing temperature.

The size and position of the endothermic peak is strongly related to annealing temperature and time.An additional third melting was observed when quenched nylon 610 was annealed at high temperature for a sufficiently long residence time.

The existence of the third melting peak suggests that more than one kind of distribution of lamella thickness may occur when quenched nylon 610 is annealed.The implications of these results in terms of crystal thickening mechanism were discussed.

PA610 Resin PA612 Resin PA1010 Resin PA1212 Resin    WECHAT:18602297376

Office: No.B11 Wealth Plaza,Weijin Road,Heping District,Tianjin,China. Zip code: 300070

E-mail:sales@lyuechem.com Tel: +0086-22-23447568 Mob: +0086-18602297376

Lyuechem Technology Co.,Ltd. Copy right © 2010-2023

Technical Support : Lyuechem津公网安备 12010102000573号

天津谷骐科技有限公司 津ICP备:18001702号-6

Scan to add WeChat